在课程群的教学中由于每门课程各自独立开展教学,缺乏知识的融合和衔接,导致学生运用综合知识解决问题的能力较弱。在课程群的教学中采用案例嵌入协同教学模式,将完整的工程案例嵌入到课程群各门课程的教学中,协同规划各门课程的教学任务,每门课程再围绕案例展开研究性教学。通过嵌入的工程案例衔接各门课程的知识点,帮助学生建构完整的知识体系,强化工程应用的概念；同时通过研究性教学,培养学生分析问题和解决问题的能力,两部分相结合,提高了学生运用综合知识解决复杂问题的能力。     

强化研磨加工中喷射角度对GCr15轴承钢板塑性变形的影响

利用ABAQUS有限元仿真软件研究不同喷射角度强化研磨加工GCr15轴承钢板过程的塑性变形,得到不同喷射角度与等效塑性应变沿真实路径距离的关系,并通过拉伸试验进行验证。喷射角度为90°的强化研磨加工伸长率为1.4%,相比未经过强化研磨加工的伸长率数值缩减了2.0%。断口收缩率由空白组的4.9%降低到喷射角为90°的2.2%。结合仿真和试验可知,强化研磨加工中喷射角度越大,塑性变形能力越低,材料加工越难。     

制备金属铪的新进展

金属铪在核能、航天以及军工领域有着得天独厚的优势,国内外对于金属铪的研究正如火如荼的进行。锆铪相伴而生,本文介绍了锆铪的火法和湿法分离,综述了金属热还原法和熔盐电脱氧法制备金属铪通过熔盐电解法、碘化精练法、电子束熔炼法精炼金属铪,就各种方法的优缺点和绿色生产的需求来看,新型熔盐电脱氧法和联合精炼法是值得发展和探究的方向。     

High‐performance thermosets with tailored properties derived from methacrylated eugenol and epoxy‐based vinyl ester

A renewable chemical, eugenol, is methacrylated to produce methacrylated eugenol (ME) employing the Steglich esterification reaction without any solvent. The resulting ME is used as a low‐viscosity co‐monomer to replace styrene in a commercial epoxy‐based vinyl ester resin (VE). The volatility and viscosity of ME and styrene are compared. The effect of ME loading and temperature on the viscosity of the VE–ME resin is investigated. Moreover, the thermomechanical properties, curing extent and thermal stability of the fully cured VE–ME thermosets are systematically examined. The results indicate that ME is a monomer with low volatility and low viscosity, and therefore the incorporation of ME monomer in VE resins allows significant reduction of viscosity. Moreover, the viscosity of the VE–ME resin can be tailored by adjusting the ME loadings and processing temperature to meet commercial liquid molding technology requirements. The glass transition temperatures of VE–ME thermosets range from 139 to 199 °C. In addition, more than 95% of the monomer is incorporated and fixed in the crosslinked network structure of VE–ME thermosets. Overall, the developed ME monomer exhibits promising potential for replacing styrene as an effective low‐viscosity co‐monomer. The VE–ME resins show great advantages for use in polymer matrices for high‐performance fiber‐reinforced composites. This work is of great significance to the vinyl ester industry by providing detailed experimental support. © 2018 Society of Chemical Industry     

焙烧铁尾矿制备透水砖试验研究

为了改善尾矿制砖的力学性质，解决尾矿堆积问题，采用焙烧铁尾矿、水泥和粉煤灰为胶凝材料，2.36~4.75 mm粒级铁尾矿为粗骨料，通过搅拌、成型和养护工艺制备透水砖，探究了焙烧铁尾矿用量、水胶比、目标孔隙率和振动时间对透水砖性能的影响，对比未焙烧尾矿制备透水砖的性能。结果表明：① 焙烧尾矿制备透水砖最佳试验条件为：焙烧尾矿掺量60%，振动时间40 s、水胶比0.3，目标孔隙率20%；此时，透水砖抗折强度为3.34 MPa，符合国家标准Rf3.0，抗压强度为15.44 MPa，符合国家标准MU15，透水系数为2.58×10-2 cm/s，符合国家标准A级标准，实测孔隙率为23.41%。② 焙烧尾矿掺量为60%时效果最佳；未焙烧尾矿掺量为50%时效果最佳，抗折、抗压强度分别为3.38 MPa和14.54 MPa，透水系数符合国家A级标准；焙烧尾矿比未焙烧尾矿多替代水泥10%的情况下，力学性能焙烧尾矿透水砖较好，而透水性能则未焙烧尾矿透水砖较好。     

Microwave dielectric properties of SrLa[Ga1−x(Mg0.5Ti0.5)x]O4 and SrLa[Ga1−x(Zn0.5Ti0.5)x]O4 (x = 0.2-0.8) ceramics

SrLa[Ga_1−x(R_0.5Ti_0.5)_x]O₄ (R = Mg, Zn) ceramics were prepared by a standard solid state sintering method. The single-phase ceramics with K₂NiF₄-type layered perovskite structure and I4/mmm space group were obtained, indicating that SrLa(R_0.5Ti_0.5) and SrLaGaO₄ can form the unlimited solid solutions. With increasing x for R = Mg and Zn, ε_r increases monotonously, the Qf value first increases and then decreases, while τ_f increases from a negative to a positive value. The optimized microwave dielectric properties were obtained as following: ε_r = 23.3, Qf = 89 400 GHz, τ_f = −0.8 ppm/°C for SrLa[Ga_0.6(Mg_0.5Ti_0.5)_0.4]O₄ and ε_r = 23.3, Qf = 76 200 GHz, τ_f = 0.2 ppm/°C for SrLa[Ga_0.7(Zn_0.5Ti_0.5)_0.3]O₄, indicating that the present solid solution ceramics are the promising candidates as microwave resonator materials for the telecommunication applications.     

Fine-tuned,molecular-composite,organosilica membranes for highly efficient propylene/propane separation via suitable pore size

Fine-tuned, molecular-composite, organosilica membranes were fabricated via the co-condensation of organosilica precursors bis(triethoxysilyl)acetylene (BTESA) and bis(triethoxysilyl)benzene (BTESB). Fourier transform infrared and UV–vis spectra confirmed the co-condensation behaviors of BTESA and BTESB. The evolution of the network structure indicated that the incorporated BTESB decreased the membrane pore size, which was determined by a modified gas translation model according to the steric effect of the phenyl groups. The incorporation of BTESB to BTESA finely tuned the membrane structure and endowed the resultant composite membrane with improved separation properties. The BTESAB 9:1 membrane (molar ratio of BTESA/BTESB was 9:1) exhibited high C₃H₆ permeance at 4.5 × 10⁻⁸ mol m⁻² s⁻¹ Pa⁻¹ and a C₃H₆/C₃H₈ permeance ratio of 33 at 50°C. One of the most important developments of this study involved clearly defining the relationship between membrane pore size and C₃H₆/C₃H₈ separation performance for organosilica membranes in single and binary separation systems.     

某含锌锡多金属硫化矿石锌浮选试验研究

某含锌锡多金属硫化矿石Zn、Sn、Fe、S含量分别为6.04%、1.05%、29.33%、19.08%，锌主要以铁闪锌矿、闪锌矿的形式存在，锡主要以锡石的形式存在，铁主要以黄铁矿、磁黄铁矿等形式存在，其中的金属矿物共生关系密切，相互包裹现象普遍。为确保不影响后续选锡，对锌浮选流程进行了试验研究。结果表明：矿石在磨矿细度为-0.074 mm占80%的情况下，采用预先脱硫—锌硫混浮再分离流程处理，在选择硫酸铜为锌矿物活化剂、丁基黄药为捕收剂、松醇油为起泡剂、石灰为黄铁矿抑制剂的情况下，经1段脱硫、2粗1扫锌硫混浮、1粗2精锌硫分离，锌硫分离精选尾矿与锌硫混浮扫选精矿2次精选后锌硫分离，最终获得锌精矿Zn品位47.06%、回收率90.76%，试验指标良好。